PERLINDUNGAN WARNA PADA KAIN WARNA ALAMI INDIGO DENGAN NANO PARTIKEL SENG OKSIDA YANG DISINTESIS DENGAN METODE SOL-GEL Color Protection of Cotton Dyed with Indigo Natural Dye using Zinc Oxide Nanoparticles synthesized via Sol-Gel Method Section Articles

##plugins.themes.academic_pro.article.main##

Renung Reningtyas
Edia Rahayuningsih
Yuni Kusumastuti
Indriana Kartini

Abstract

ABSTRAK


Seiring dengan meningkatnya kesadaran manusia terhadap dampak dari penggunaan zat warna sintetik, zat warna alami yang lebih ramah lingkungan mulai digunakan kembali untuk pewarnaan tekstil, khusunya pada industri batik di Indonesia. Salah satu zat warna alami yang popular digunakan adalah zat warna alami indigo. Pewarnaan kain dengan indigo alami memiliki tingkat ketahanan luntur terhadap pencucian yang baik namun ketahanan warna terhadap paparan sinar masih kurang baik. Penambahan agen anti ultra-violet (anti-UV)  merupakan salah satu cara untuk meningkatkan ketahanan warna kain akibat paparan sinar. Pada penelitian ini, nano partikel seng oksida (ZnONP) diaplikasikan pada kain batik yang telah diwarnai dengan indigo alami sebagai anti-UV untuk melindungi warna kain. ZnONP disintesis menggunakan metode sol-gel dan aplikasi ke kain dilakukan dengan metode perendaman. Distribusi ukuran partikel ZnO dianalisis menggunakan teknik direct light scattering. Konsentrasi dispersi ZnONP untuk perendaman divariasi pada kisaran 50 – 1000 ppm. Efek ZnONP sebagai anti-UV dilakukan dengan uji pudar warna dimana kain indigo diberi paparan sinar UV-A selama 200 jam dalam fotoreaktor. Semakin tinggi konsentrasi ZnONP, semakin baik perlindungan warna yang diberikan. Konsentrasi dispersi ZnONP sebanyak 500 ppm elah memberikan hasil perlindungan warna yang cukup baik.


ABSTRACT


Along with the increasing of awareness on the utilization of synthetic dyes, the more environmentally friendly natural dye are starting to revive for textile coloring, especially in the batik industry in Indonesia. One of the popular natural dyes used is natural indigo dye. Fabric dyeing with natural indigo has a good level of fastness to washing but the color resistance to light exposure is still poor. The addition of an anti-ultraviolet (anti-UV) agent is one way to increase the color fastness of the fabric due to exposure to light. In this study, zinc oxide nanoparticles (ZnONPs) were applied to cotton that had been dyed with natural indigo as an anti-UV to protect the color of the fabric. ZnONP was synthesized using the sol-gel method and the application to the fabric was carried out by the dip coating method. The particle size distribution was measured using direct light scattering technique. The concentration of ZnONP dispersion for coating was varied in the range of 50 – 1000 ppm. The effect of ZnONP as an anti-UV was carried out by photofading test in which indigo fabric was exposed to UV-A light for 200 hours in a photoreactor. Higher concentration of ZnONP provides better color protection, however, increasing ZnONP concentration from 500 ppm to 1000 ppm gave insignificant result.

##plugins.themes.academic_pro.article.details##

Author Biographies

Renung Reningtyas, Universitas Pembangunan Nasional "Veteran"

¹Departemen Teknik Kimia Fakultas Teknik Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

²Jurusan Teknik Kimia Fakultas Teknik Indistri Universitas Pembangunan Nasional “Veteran” Yogyakarta, Condongcatur, Yogyakarta 55283, Indonesia

Edia Rahayuningsih, Universitas Gadjah Mada

¹Departemen Teknik Kimia Fakultas Teknik Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

3Indonesia Natural Dye Institute (INDI), Integrated Research and Testing Laboratory (LPPT), Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

Yuni Kusumastuti, Universitas Gadjah Mada

¹Departemen Teknik Kimia Fakultas Teknik Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

3Indonesia Natural Dye Institute (INDI), Integrated Research and Testing Laboratory (LPPT), Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

Indriana Kartini, Universitas Gadjah Mada

3Indonesia Natural Dye Institute (INDI), Integrated Research and Testing Laboratory (LPPT), Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

4Departemen Kimia Fakultas Matematika dan Pengetahuan Alam Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia

How to Cite
Reningtyas, R., Rahayuningsih, E., Kusumastuti, Y., & Kartini, I. (2021). PERLINDUNGAN WARNA PADA KAIN WARNA ALAMI INDIGO DENGAN NANO PARTIKEL SENG OKSIDA YANG DISINTESIS DENGAN METODE SOL-GEL . Prosiding Seminar Nasional Industri Kerajinan Dan Batik, 3(1), C.12 1-11. Retrieved from https://proceeding.batik.go.id/index.php/SNBK/article/view/124